carbon aramid fabric, carbon fiber 3k tr30s, aramid fiber 1260 dtex, carbon aramid fabric twill 210 g
TECHNICAL CHARACTERISTICS
Areal weight: 210 g / m2
Weaving style: Twill 2X2
Width: 1.20 meters
Warp type of yarn: 3K TR30S carbon fiber + 1111 aramid fiber, 1260 dtex
Weft type of yarn: 3K TR30S carbon fiber + 1111 aramid fiber, 1260 dtex
Warp reinforcement ratio: 50%
Weft reinforcement ratio: 50%
Warp thread count: 3.2+3.2=6.4 ends (threads) / cm
Weft thread count: 3.2+3.2=6.4 ends (threads) / cm
Fiber content by weight: 61% carbon / 39% aramid
Weaving style: Twill 2X2
Width: 1.20 meters
Warp type of yarn: 3K TR30S carbon fiber + 1111 aramid fiber, 1260 dtex
Weft type of yarn: 3K TR30S carbon fiber + 1111 aramid fiber, 1260 dtex
Warp reinforcement ratio: 50%
Weft reinforcement ratio: 50%
Warp thread count: 3.2+3.2=6.4 ends (threads) / cm
Weft thread count: 3.2+3.2=6.4 ends (threads) / cm
Fiber content by weight: 61% carbon / 39% aramid
TYPICAL MECHANICAL PROPERTIES OF FIBERS USED
Carbon
Tensile strength (MPa): 4410
Tensile modulus (GPa): 235
Elongation at break (%): 1.9
Aramid
Tensile strength (MPa): 2987
Tensile modulus (GPa): 91
Elongation at break (%): 3.10
Carbon
Tensile strength (MPa): 4410
Tensile modulus (GPa): 235
Elongation at break (%): 1.9
Aramid
Tensile strength (MPa): 2987
Tensile modulus (GPa): 91
Elongation at break (%): 3.10
Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.